ASTM A105/A105M - 24 - Tienda AENOR

Contacta con Nosotros (+34) 914 326 036

Aviso:	Las normas ASTM en lectura se visualizan a través del área de cliente. Los archivos no se pueden descargar
Fecha edición:	2024-04-15 Anulada
Fecha cancelación:	2024-04-15
Idiomas disponibles:	Inglés
Resumen:	This specification covers standards for forged carbon steel piping components, that is, flanges, fittings, valves, and similar parts, for use in pressure systems at ambient and higher-temperature service conditions. Materials shall be subjected to heat treatment (annealing, normalizing, tempering, or quenching). Material shall conform to carbon, manganese, phosphorus, sulfur, silicon, copper, nickel, chromium, molybdenum and vanadium contents. The forgings shall be subjected to tension, hardness and hydrostatic tests, with the latter applicable when required. Material shall adhere to tensile strength, yield strength, elongation, reduction of area, and hardness requirements. Guidelines for retreatment, repair by welding, and product marking are given.
Keywords:	pipe fittings, steel; piping applications; pressure containing parts; steel flanges; steel forgings, carbon; steel valves; temperature service applications, elevated; temperature service applications, high;
Scope:	1.1 This specification2 covers forged carbon steel piping components for ambient- and higher-temperature service in pressure systems. Included are flanges, fittings, valves, and similar parts ordered either to dimensions specified by the purchaser or to dimensional standards such as the MSS, ASME, and API specifications referenced in Section 2. Forgings made to this specification are limited to a maximum weight of 10 000 lb [4540 kg]. Larger forgings may be ordered to Specification A266/A266M. Tubesheets and hollow cylindrical forgings for pressure vessel shells are not included within the scope of this specification. Although this specification covers some piping components machined from rolled bar and seamless tubular products (see 5.2), it does not cover raw material produced in these product forms. 1.2 Supplementary requirements are provided for use when additional testing or inspection is desired. These shall apply only when specified individually by the purchaser in the order. 1.3 Specification A266/A266M covers other steel forgings and Specifications A675/A675M and A696 cover other steel bars. 1.4 This specification is expressed in both inch-pound units and SI units. However, unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished to inch-pound units. The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Note 1: The dimensionless designator NPS (nominal pipe size) has been substituted in this standard for such traditional terms as “nominal diameter,” “size,” and “nominal size.” 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ICS:	77.140.85 - Piezas forjadas
CTN:	A01.22 - A01.22
Anulaciones Normas	Anula a A0105_A0105M-23
Otras Relaciones	Es referenciada por A234/A234M - 25 Es referenciada por F0721-18R22 Es referenciada por C1847-21 Es referenciada por F1545-15AR21 Es referenciada por F1508-96R21 Es referenciada por C1617-24 Es referenciada por F1155-10R24 Es referenciada por F1565 - 00(2024) Es referenciada por A961/A961M - 25a